EFFECT OF WELDING CURRENT (SMAW) ON TENSILE STRENGTH AND MICROSTRUCTURE OF S45C STEEL

Muhaemin Al Fikri(1*), Iwan Nugraha Gusniar(2), Viktor Naubnome(3)


(1) Universitas Singaperbangsa Karawang
(2) Universitas Singaperbangsa Karawang
(3) Universitas Singaperbangsa Karawang
(*) Corresponding Author

Abstract


Welding is a metal joining technique by partially melting the parent metal and filler metal with or without additional metal and producing a continuous connection. One type of welding that is often used is SMAW (Shieled Metal Arc Welding) welding. In SMAW welding, the influence of the current used plays an important role in welding. Because it affects the results of the strength of the welded joint. This research was conducted to determine the mechanical properties of tensile testing and microstructure under the influence of different currents. In this research, the test material is S45C steel and the current variation is 90 A, 110 A, and 120 A and the type of electrode used is E7016 LB57. The results obtained from the tensile test have the optimum value at 120 A with a tensile strength of 49.43 kg/mm while 110 A with a tensile strength of 43 kg/mm and 90 A with a tensile strength of 11.04 kg/mm. for testing the microstructure seen in the welded parts and the heat affected area.

 

Keywords: variations in welding current, welding smaw, S45C, tensile strength.

Keywords


variasi arus las, las smaw, S45C, kekuatan tarik.

Full Text:

PDF

References


Andrijono, Djoko, and Ike Widyastuti. "Kekerasan dan Struktur Mikro Plat Baja Karbon Rendah 0, 16% C Hasil Bengkel Las SMAW dengan Elektroda E 309-16 ESAB Posisi Flat 1G setelah Variasi Quenching." TRANSMISI 17.1 (2021).

Effendi, Nizam. "STRUKTUR MIKRO DAN KEKERASAN BAJA S45C PADA PENGELASAN SMAW DENGAN VARIASI MEDIA QUENCH." Jurnal Ilmiah Pendidikan Teknik dan Kejuruan 12.1: 30-37.

Harsono, W., and T. Okumura. "Teknologi Pengelasan Logam, Cetakan Ke-7, PT." Pradnya Paramita, Jakarta (2004).

Rananggono, D., Mulyadi, Y., & Winarno, G. D. (2008). Studi Kekuatan Mekanik dan Struktur Mikro Hasil Pengelasan SMAW dengan Variasi Preheat dan Postheat Menggunakan Metode Pendinginan Cepat dan Pendinginan Lambat. Jurnal Tugas Akhir Institut Teknologi Surabaya.

Suharno, Suharno, and Yuyun Estriyanto. "PENGARUH VARIASI BESAR SUDUT KAMPUH V TUNGGAL TERHADAP STRUKTUR MIKRO, KEKERASAN, DAN KEKUATAN TARIK MATERIAL BAJA SS400 DENGAN METODE PENGELASAN SMAW." NOZEL Jurnal Pendidikan Teknik Mesin 2.4 (2018): 301-311.

Syahrani, Awal, Naharuddin Naharuddin, and Muhammad Nur. "ANALISIS KEKUATAN TARIK, KEKERASAN, DAN STRUKTUR MIKRO PADA PENGELASAN SMAW STAINLESS STEEL 312 DENGAN VARIASI ARUS LISTRIK." Jurnal Mekanikal 9.1 (2018).

WIRYOSUMARTO, Harsono; OKUMURA, Toshie. Teknologi pengelasan logam, PT. Pradnya Paramita, Jakarta, 2000.

Widharto, Sri. "Welding Inspection." Mitra Wacana Media (2013): 9-10


Article Metrics

Abstract view : 190 times
PDF - 71 times

DOI: https://doi.org/10.26714/traksi.22.1.2022.109-121

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 TRAKSI

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.


TRAKSI : Majalah Ilmiah Teknik Mesin

ISSN : 1693-3451 (Pinted) e-ISSN : 2579-9738 (Online)

Published by: LP2M Unimus bekerjasama dengan APTI (Asosiasi Profesi Teknik Indonesia)  

 
ADDRESS

Jl. Kasipah No. 12 Semarang

E-mail: [email protected] Call: 0248445768


Sponsors

Asosiasi Profesi Teknik Indonesia (APTI)

Website: www.apti.or.id